Sticking for the belief of Creating items of top of the range and creating buddies with people today from all over the world, we normally put the interest of shoppers in the first place for Pldc Film, Laminated Glass Interlayer Film, Eva Film, Many years of work experience, we have realized the importance of providing good quality products and the best before-sales and after-sales services.

High reputation Sgp Glass - Ionoplast interlayer film – Xiaoshi Detail:

Ionoplast interlayr film technology breaks the foreign monopoly of high strength ionoplast interlayer material for laminated safety glass, and promoting the development of the whole laminated glass industry.

It is made of ethylene and methacrylate ion copolymer, containing about 1% metallic sodium ion. Five times stronger and up to 100 times stiffer than conventional laminating materials. With this kind of strength the glass can be a more active structural element in the constructions, opening up design possibilities that didn’t exist before. Besides its strength, the ionoplast interlayer retains excellent optical and visual performance even after years of outdoor exposure. Ionoplast interlayer film is much less vulnerable to moisture exposure or yellowing over time. It is the research achievements to meet the growing market demand for security, safety, durability, aesthetics, edge stability and other aspects of laminated glass, especially in the application like hurricane glazing, glass bridge, facades, overhead glazing ,etc.

Features
• Stiffness: 100 times stiffer of conventional interlayer materials
• Tearing strength: 5 times stronger of conventional interlayer materials
• Excellent optical and visual performance
• Yellowish index(YI): <1.5
• Outstanding durability after UV radiation
• High edge stability, Good compatibility with silicon.
Product advantages
1. Tearing strength : 5 times stronger than conventional interlayer material .
2. Stiffness: 100 times stiffer than conventional interlayer material.
3. The load-bearing of laminated glass made from Ionoplast interlayer film is twice stronger than made from PVB interlayer at same thickness combination.
4. The deflection of laminated glass made fromIonoplast interlayer film is only 1/4 of laminated glass made from PVB under the same thickness and load.
5. The stress and deflection of laminated glass made from Ionoplast interlayer film are essentially same as monolithic glass at same thickness, while the laminated glass made from PVB are much greater.
6. Reduction of glass thickness, and the glass weight could be reduced by 40%.
7. Suitable for open edge development and design.
8. Reduction the number of fixing points for frameless glazing , make design more innovative and diversification .
Storage conditions
Ionoplast interlayer film should be stored at room temperature with original sealing vacuum moistureproof packing. It is recommended use material within 24months from the date of production to avoid the decline of adhesion. Please properly seal and pack unused materials and store them in cool place to prevent the material from being exposed to the environment and absorbing moisture, which may resulting in adhesion reduced.Control the moisture of material not over 0.2%, Otherwise the adhesion may go down and have bubbles during laminating. It is also recommended that testing the moisture content and the adhesion property of Ionoplast interlayer film before production if it has been stored for a long time from the production date. If the moisture content exceeds 0.2%, it is not recommended to use.

Technical Data

	Item	Test Method	Safeglas ™ MG
Physicial	Roll Length		50-100 m
	Max.Width		2400 mm
	Thickness	Micrometer	0.76-1.52 mm
	Specific Gravity	ASTM792	0.93-0.98 g/cm3
	Hardness(1.52mm)	ASTMD2240	65 Shore D
Mechanical	Elongation at Break	ASTMD683	≧ 300%
	Young modulus	ASTMD683	>300 Mpa
	Shear modulus	ASTMD683	42.7 N/mm2
	Bending modulus	ASTMD683	345 Mpa(23 ℃)
	Shear strength	ASTMD683	50 MJ/m2
	Tensile strength	ASTMD683	≧ 30 Mpa
Thermal	Coeffcient of thermal expansion	ASTMD831	10-15*103cm/cm ℃
	Thermal deflection temperature	ASTMD831	40 ℃
	Melt point	ASTMD831	94 ℃
	Flash point	ADTMD1929	470 ℃
Optical	YI	JC/T2166-2013	<15%
	Refractive Index	JC/T2166-2013	1.5%(20 ℃)
	Light Transmittance	JC/T2166-2013	90.2 % (0.76mm)
	Haza	JC/T2166-2013	<0.5 % (0.76mm)
	UV filtering	JC/T2166-2013	>99 % (380nm)

Product Specifications

Thickness (mm)	Max.Width (mm)	Length(m)	Packing
0.76/0.89/1.14	2400	100	Inside: Tinfoil vacuum Outside: Plywood case
1.35
1.52		50
Application: Facades, Hurrican Glazing, Sunroom Glazing, Jumbo Glass, etc.